توضیحات

Type

Color

BET Surface area (m ² / g) Pore diameter (nm)

Pore volume (cm ³ / g)

Synthesis method

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

XRD

   X-ray diffraction analysis XRD pattern for Mno /RGO contains broad peaks at 2-theta = 25 ⁰, 31.2⁰, 37.0 ⁰ and 65.4 ⁰. These correspond to ô-Mn02, which is a 2D layered structure with stabilizing cations intercalated between the Mn06 octahedral sheets. For the XRD profile of the Mn02/RGO sample, a weak peak at 2-theta = 21.7 ⁰ appears, which can be ascribed to the irregular stacking of RGO

 

 

Performance comparision of catalysts

Comparison ofthe performance of different catalysts

Oxygen reduction reaction (ORR)

kOH 0. 1 M. electrolyte

 

 

 

To evaluate the electrocatalytic activity of different catalyst towards oxygen reduction reaction, the cyclic voltammograms (CVs) of five catalysts of Mn02, MnoJCA, CoA-MnoJCA, Mno /RGO and activated carbon were recorded in the presence (O -saturated) of oxygen in 0. I M KOH electrolyte solution at scan rate of 20 mV/s. As can be seen in the cyclic voltammograms (CVs), on the surface of bare carbon cloth electrode in N2-saturated KOH solution, no noticeable oxygen reduction peak is observed while a weak reduction wave is appeared in the 02-purged KOH electrolyte which could be ascribed to the catalytic role of carbon-based substrates for ORR. Among these five catalysts, the RGO a-MnO catalyst shows the most obvious cathodic peak for oxygen reduction, which is in the potential range of 0.2 to -0.6 V

NOVASI